eSUN yellow HIPS filament is a soluble 3D printing material used to produce support structures and standalone products alike. It has mechanical properties similar to ABS while being stronger than it. It is a professional yet budget consumable widely compatible with FDM printers equipped with a heated bed.
eSUN yellow HIPS can be combined with ABS for printing intricate geometries, overhangs and interior cavities using dissolvable support structures. It features a low warping rate and a low water absorption rate. It allows hands-free removal by dipping the printed models in Limonene. It delivers clean and smooth surfaces. Printing with a PEI build surface will strongly increase the layer adhesion. It comes in a vacuum-packed bag coiled around a 1kg spool.
This yellow lucky cat has been printed using eSUN HIPS. As you can see, the final surface finish is quite glossy.
Specifications
eSUN yellow HIPS technical data
- Printing temperature: 220 – 260 °C
- Heated bed temperature: 90 – 110°C recommended
- Filament density: 1.05 g/cm³
- Heat Distortion Temperature (0.45MPa): 80 °C
- Melt Flow Index: 3 g/10min (800°C/5KG)
- Tensile Strength: 27 MPa
- Elongation at Break: 55%
- Flexural Strength: 39 MPa
- Flexural Modulus: 2,280 MPa
- IZOD Impact Strength: 11 KJ/㎡
Spool specs
- Filament diameter: 1.75mm
- Dimensional Accuracy: ±0.05
- Spool weight: 1kg
- Color name: Yellow
- Color attribute: Solid
The eSUN yellow HIPS is supplied in 1kg filament spools. Each spool is vacuum-packed in a desiccant bag for storage and freshness.
Filament diameter | 1.75mm |
Color attribute | Solid |
Color name | Yellow |
Dimensional Accuracy | ±0.05 |
Elongation at Break | 55% |
Filament density | 1.05 g/cm³ |
Flexural Modulus | 2,280 MPa |
Flexural Strength | 39 MPa |
Heat Distortion Temperature (0.45MPa) | 80 °C |
Heated bed temperature | 90 – 110°C recommended |
IZOD Impact Strength | 11 KJ/㎡ |
Melt Flow Index | 3 g/10min (800°C/5KG) |
Printing temperature | 220 – 260 °C |
Spool weight | 1kg |
Tensile Strength | 27 MPa |